F58
Inventory F58 Specifications, Suppliers F58 Datasheet Chemical, Stocklist F58 Properties Forgings Ex-stock & Plate F58 Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards - ASTM A182 - 2018.or by agreement.100% Ultrasonic test ASTM
| Product parameters | |
| Material Category:: | Superalloy |
| Steel Grade: | F58 |
| Material Technical Standards:: | ASTM |
| Specification Code:: | ASTM A182 - 2018 |
| Place of Origin: | USA |
Description
TECHNICAL DATASHEET - ASTM A182 Grade F58
Material Technical Standards - ASTM A182 - 2018
Steel Material Type - 24Cr-22Ni-6.0Mo Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
Chemical Composition ( Mass Weight % )
C (％): ≤ 0.030
Mn (％): 2.00 ~ 4.00
Si (％): ≤ 1.00
P (％)≤: 0.035
S (％)≤: 0.020
Ni (%): 21.0 ~ 24.0
Cr (%): 23.0 ~ 25.0
Mo (%): 5.20 ~ 6.20
Nb (%): -
N (%): 0.35 ~ 0.60
Cu (%): 1.00 ~ 2.50
W (%): 1.50 ~ 2.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 750
Yield strength, σ0.2/MPa: 420
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1120 ~ 1180 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1200mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers, Email: sales@cnlhss.com
Material Technical Standards - ASTM A182 - 2018
Steel Material Type - 24Cr-22Ni-6.0Mo Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
Chemical Composition ( Mass Weight % )
C (％): ≤ 0.030
Mn (％): 2.00 ~ 4.00
Si (％): ≤ 1.00
P (％)≤: 0.035
S (％)≤: 0.020
Ni (%): 21.0 ~ 24.0
Cr (%): 23.0 ~ 25.0
Mo (%): 5.20 ~ 6.20
Nb (%): -
N (%): 0.35 ~ 0.60
Cu (%): 1.00 ~ 2.50
W (%): 1.50 ~ 2.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 750
Yield strength, σ0.2/MPa: 420
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1120 ~ 1180 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1200mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers, Email: sales@cnlhss.com