RAW MATERIAL - AMS 5719
TECHNICAL SPECIFICATIONS - AMS 5719C
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass fraction %)
C (％): 0.08 ~ 0.13
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Mo (％): 1.50 ~ 2.00
Ni (%): 2.00 ~ 3.00
V (％): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 1100
Yield strength, σs ≥ Mpa: 860
Elongation, δ5 ≥ (%): 12.0
Hardness HBW: 341 ~ 375
Hardness HBS: 310 max in annealed condition
HEAT TREATMENT PRACTICE
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool
TECHNICAL SPECIFICATIONS - AMS 5719C
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass fraction %)
C (％): 0.08 ~ 0.13
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Mo (％): 1.50 ~ 2.00
Ni (%): 2.00 ~ 3.00
V (％): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 1100
Yield strength, σs ≥ Mpa: 860
Elongation, δ5 ≥ (%): 12.0
Hardness HBW: 341 ~ 375
Hardness HBS: 310 max in annealed condition
HEAT TREATMENT PRACTICE
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool