AMS 5643V
Specifications AMS 5643V Datasheet, AMS 5643V Chemical, AMS 5643V Properties Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materia
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | AMS 5643V |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 5643V |
| Place of Origin: | USA |
Description
MATERIAL TECHNICAL DATASHEET - AMS 5643
MATERIAL CATEGORY - Martensitic steel
INVENTORY ON SALE - Diam.10 ~ 210mm
HS CODE - 72221100 / 72221900 / 72222000
Aerospace technical standards - AMS 5643V
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Cu (％): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AT RM.
Heat condition: H900 / H1000 / H1050 / H1100 H 1150
Tensile strength, σb/MPa: ≥1310 (+ H900)
Yield strength, σ0.2/MPa: ≥1170
Elongation, δ (％): ≥ 10.0
Reduction of area, ψ (％): ≥ 40.0
Hardness / HRC: ≥40
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
Round bar / wire: Diam.5.5 ~ 400mm
Heavy/middle plate via hot rolled: T60 - 200mm X W60 - 1200mm X L1000 - 6000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
MATERIAL CATEGORY - Martensitic steel
INVENTORY ON SALE - Diam.10 ~ 210mm
HS CODE - 72221100 / 72221900 / 72222000
Aerospace technical standards - AMS 5643V
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Cu (％): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AT RM.
Heat condition: H900 / H1000 / H1050 / H1100 H 1150
Tensile strength, σb/MPa: ≥1310 (+ H900)
Yield strength, σ0.2/MPa: ≥1170
Elongation, δ (％): ≥ 10.0
Reduction of area, ψ (％): ≥ 40.0
Hardness / HRC: ≥40
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
Round bar / wire: Diam.5.5 ~ 400mm
Heavy/middle plate via hot rolled: T60 - 200mm X W60 - 1200mm X L1000 - 6000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com