2S130
Descriptions 2S130 datasheet, 2S130 Chemical, 2S130 Properties steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standa
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | 2S130 |
| Material Technical Standards:: | BS EN |
| Specification Code:: | BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001 |
| Place of Origin: | England |
Description
TECHNICAL SPECIFICATION DATASHEET - BS 2S130
MATERIAL CATEGORY - Aerospace "S" Series alloy steel
MATERIAL SPECIFICATIONS - BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): 0.20 ~ 1.00
Mn (％): 0.50 ~ 2.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 17.0 ～ 19.0
Ni (％): 8.00 ～ 11.0
Mo (％): ≤ 1.00
Nb (%): 10 X C ~ 1.10
HEAT TREATMENT AND MECHANICAL PROPERTIES
Heat treatment temperature and cooling: Solution treatment 1050 Deg. W
Yield strength, σb≥/MPa: 540
Tensile strength, σ0.2≥/MPa: 210
Elongation, δ5 (%)≥: 35.0
Hardness ≤HBW: 183
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com
MATERIAL CATEGORY - Aerospace "S" Series alloy steel
MATERIAL SPECIFICATIONS - BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): 0.20 ~ 1.00
Mn (％): 0.50 ~ 2.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 17.0 ～ 19.0
Ni (％): 8.00 ～ 11.0
Mo (％): ≤ 1.00
Nb (%): 10 X C ~ 1.10
HEAT TREATMENT AND MECHANICAL PROPERTIES
Heat treatment temperature and cooling: Solution treatment 1050 Deg. W
Yield strength, σb≥/MPa: 540
Tensile strength, σ0.2≥/MPa: 210
Elongation, δ5 (%)≥: 35.0
Hardness ≤HBW: 183
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment