X3MnCrNiMoN20-13
Ex-stock X3MnCrNiMoN20-13 Specifications, Datasheet X3MnCrNiMoN20-13 Forging Bar, Property X3MnCrNiMoN20-13 From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | X3MnCrNiMoN20-13 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312 |
| Place of Origin: | Germany |
Description
TECHNICAL DATA SHEET - Grade X3MnCrNiMoN20-13
HSN CODE - 72221100 / 72222000
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - magnetic stainless steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): 0.30 ~ 0.60
Mn (％): 18.5 ~ 22.0
P (％) ≤: 0.030
S (％) ≤: 0.008
Cr (％): 13.0 ~ 16.0
Ni (％): 0.25 ~ 0.50
Mo (%): 0.35 ~ 0.60
N (%): 0.32 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 1050 ~ 1150 Deg.C
Tensile strength, σb/ ≥ MPa: 900
Yield strength, σ0.2/ ≥ MPa: 770
Elongation, δ (％) ≥: 25.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 277 Min.
METHOD OF MELT
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 400mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
HSN CODE - 72221100 / 72222000
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - magnetic stainless steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): 0.30 ~ 0.60
Mn (％): 18.5 ~ 22.0
P (％) ≤: 0.030
S (％) ≤: 0.008
Cr (％): 13.0 ~ 16.0
Ni (％): 0.25 ~ 0.50
Mo (%): 0.35 ~ 0.60
N (%): 0.32 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 1050 ~ 1150 Deg.C
Tensile strength, σb/ ≥ MPa: 900
Yield strength, σ0.2/ ≥ MPa: 770
Elongation, δ (％) ≥: 25.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 277 Min.
METHOD OF MELT
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 400mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.