Specifications T911 datasheet, T911 Chemical, T911 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | T911 |
| Material Technical Standards:: | ASTM |
| Specification Code:: | AISI T911 |
| Place of Origin: | USA |
Description
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - AISI T911
MATERIAL CATEGORY - Low alloy seamless pipe for boiler, heat exchanger, condenser
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.09 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 8.00 ~ 9.50
Ni (％): ≤ 0.40
Mo (％): 0.90 ~ 1.10
W (％): 0.90 ~ 1.10
V (%): 0.15 ~ 0.25
Nb (%): 0.06 ~ 0.10
B (%): 0.0003 ~ 0.006
N (%): 0.040 ~ 0.090
Others (%): Al ≤0.04
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb≥/MPa: 620
Yield strength, σ0.2≥/MPa: 440
Elongation, δ≥(％): 20.0
Hardness ≤|HBW: 179
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
TYPICAL APPLICATIONS
Boiler, heat exchanger, condenser
Chemical equipments
Electronics
Bolt and nut
Valve and forgings
FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T4 - 300mm X W80 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com
TECHNICAL SPECIFICATION DATASHEET - AISI T911
MATERIAL CATEGORY - Low alloy seamless pipe for boiler, heat exchanger, condenser
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.09 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 8.00 ~ 9.50
Ni (％): ≤ 0.40
Mo (％): 0.90 ~ 1.10
W (％): 0.90 ~ 1.10
V (%): 0.15 ~ 0.25
Nb (%): 0.06 ~ 0.10
B (%): 0.0003 ~ 0.006
N (%): 0.040 ~ 0.090
Others (%): Al ≤0.04
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb≥/MPa: 620
Yield strength, σ0.2≥/MPa: 440
Elongation, δ≥(％): 20.0
Hardness ≤|HBW: 179
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
TYPICAL APPLICATIONS
Boiler, heat exchanger, condenser
Chemical equipments
Electronics
Bolt and nut
Valve and forgings
FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T4 - 300mm X W80 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com