STR 616
Ex-stock STR 616 Blade, Specifications STR 616 Datasheet, STR 616 Properties forging Bar Plate machined, Exporters Technical specifications - KS D3731 - 2002 / 2007. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, St
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | STR 616 |
| Material Technical Standards:: | KS |
| Specification Code:: | KS D3731 - 2002/2007 |
| Place of Origin: | Korea |
Description
TECHNICAL DATA SHEET - KS D3731 Grade STR 616
TECHNICAL SPECIFICATIONS - KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
HS code: 72221100 / 7219 1100
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.20 ~ 0.25
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 11.0 ~ 13.0
Ni (％): 0.50 ~ 1.00
Mo (%): 0.75 ~ 1.25
W (%): 0.75 ~ 1.25
V (%): 0.20 ~ 0.30
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1020 ~ 1070 Deg.C, air or oil cooled
Aged 600 Deg. C Min., air cooling
Tensile strength, σb/ ≥ MPa: 885
Yield strength, σ0.2/ ≥ MPa: 735
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 25.0
Hardness ≤ (HBW): 341 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 500mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
TECHNICAL SPECIFICATIONS - KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
HS code: 72221100 / 7219 1100
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.20 ~ 0.25
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 11.0 ~ 13.0
Ni (％): 0.50 ~ 1.00
Mo (%): 0.75 ~ 1.25
W (%): 0.75 ~ 1.25
V (%): 0.20 ~ 0.30
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1020 ~ 1070 Deg.C, air or oil cooled
Aged 600 Deg. C Min., air cooling
Tensile strength, σb/ ≥ MPa: 885
Yield strength, σ0.2/ ≥ MPa: 735
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 25.0
Hardness ≤ (HBW): 341 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 500mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.