F54 & S39274 Duplex Stainless Steel
Inventory F54 Specifications, Suppliers F54 Datasheet Chemical, Stocklist F54 Properties Forging Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards - ASTM A182
| Product parameters | |
| Material Technical Standards:: | ASTM A182/ A182M |
| Melting Process Route:: | BEF + AOD /+ ESR |
| Heat Treatment Practice:: | Solution 1050 ℃, water or oil cooled |
| Ultrasonic Test Standard:: | EN 10228-3, GB/T 4162-2008, ASTM E2375, ASTM A745. EN 10307-2001 |
| Standard Export Packing Way:: | Wooden box / tray / pallet free from fumigation |
| Production Lead Time:: | Within 55 days after 40% deposit prepayable |
Description
F54 (S39274) is defined to Ferritic-Austenitic Stainless steel series, this grades offers Corrosion resistant & Heat resistant quality & Polishing performance. Forms of Round bars, Flat bars, and forgings can be available.
Material Technical Datasheet - ASTM A182 Grade F54
Chemical Composition ( Mass Weight % )
C (％): ≤ 0.030, Mn (％): ≤ 1.00, Si (％): ≤ 0.80, P (％)≤: 0.030, S (％)≤: 0.010
Ni (%): 6.00 ~ 8.00, Cr (%): 24.0 ~ 26.0, Mo (%): 2.50 ~ 3.50
N (%): 0.24 ~ 0.32, Cu (%): 0.20 ~ 0.80, W (%): 1.50 ~ 2.50
Typical Mechanical Properties
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 800
Yield strength, σ0.2/MPa: 550
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 310 max.
HEAT TREATMENT PRACTICE
Condition: solution annealing 1050 ~ 1125 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
Product Shapes & Dimensions
Round bar / Wire rod (Diameter): 5.5mm ~ 650mm
Square bar / Flat bar: 10mm to 630mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Material Technical Datasheet - ASTM A182 Grade F54
Chemical Composition ( Mass Weight % )
C (％): ≤ 0.030, Mn (％): ≤ 1.00, Si (％): ≤ 0.80, P (％)≤: 0.030, S (％)≤: 0.010
Ni (%): 6.00 ~ 8.00, Cr (%): 24.0 ~ 26.0, Mo (%): 2.50 ~ 3.50
N (%): 0.24 ~ 0.32, Cu (%): 0.20 ~ 0.80, W (%): 1.50 ~ 2.50
Typical Mechanical Properties
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 800
Yield strength, σ0.2/MPa: 550
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 310 max.
HEAT TREATMENT PRACTICE
Condition: solution annealing 1050 ~ 1125 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
Product Shapes & Dimensions
Round bar / Wire rod (Diameter): 5.5mm ~ 650mm
Square bar / Flat bar: 10mm to 630mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.