Aerospace Quality AMS 5613 Martensitic Steel
Description AMS 5613 Stock list Flat bars Ex-stock, AMS 5613 Suppliers Inventory Wire rod from Steel melting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test.
| Product parameters | |
| Material Category:: | Martensitic Stainless Steel |
| Stocklist & Inventory Available:: | Diameter 15 ~ 230mm |
| Min. order quantity Per Batch:: | 500 kg |
| Product Shapes:: | Round bars, Tube, Forgings |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 45 days after 30% deposit prepayable |
Description
AMS 5613 is usually produced by EAF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace. AMS 5613 is used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace. AMS 5613 is used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Technical Standard: AMS 5613
All Grades Equivalents
| DIN | ASTM | AISI | UNS | JIS | Other |
|---|---|---|---|---|---|
| - | Grade 403 | 403 | S40300 | SUS 403 | AMS 5613 10705BA/10705BC |
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.15 | ≤ 0.50 | ≤ 1.00 | ≤ 0.040 | ≤ 0.030 | 11.5 ～ 13.0 | ≤ 0.60 | - | - |
Mechanical Properties
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealed | ≥ 480 | ≥ 275 | ≥ 20.0 | ≥ 45.0 | - | ≤ 200 |
| Q+T 1 | ≥ 650 | ≥ 550 | ≥ 15.0 | ≥ 45.0 | ≥ 35 | 201 ～ 248 |
| Q+T 2 | ≥ 650 | ≥ 550 | ≥ 20.0 | ≥ 60.0 | ≥ 78 | 217 ～ 248 |
Shapes & Dimensions:
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 1.0 ~ 13mm
Square bar / Flat bar: 5mm to 550mm
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Length: Fixed length or random length or based on the customer's special requirement.