X5CrNiMo16-5-1 / 1.4418 Stainless Steel Shaft
Description X5CrNiMo16-5 Datasheet - Chemical Properties from Steelmaking, 1.4418 Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined.
| Product parameters | |
| Place of Origin: | P.R. China |
| Melting Process Route:: | BEF + AOD / +ESR |
| Min. order quantity Per Batch:: | 1300 KG |
| Certification:: | MTR, COC, Certificate of origin, Form A/E, Invoice, Packing list |
| Production Lead Time:: | Within 55 days after 40% deposit prepayable |
Description
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
MARTENSITIC STAINLESS STEEL - DIN X5CrNiMo16-5-1 / EN 1.4418
MATERIAL SPECIFICATIONS - DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.06, Si (％): ≤ 0.70, Mn (％): ≤ 1.50, P (％)≤: 0.040, S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0, Ni (％): 4.00 ~ 6.00, Mo (％): 0.80 ~ 1.50, N (％): ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: Quenched and tempered +T900
Tensile strength, Rm,σb/MPa: 900 ~ 1100
Yield strength, Re, σ0.2≥/MPa: 700
Elongation, δ5≥(％): 14.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 60
Hardness HBS30:
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 ~ 1000mm X L1000 ~ 4000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.