Specifications N08801 Datasheet, N08801 Chemical, N08801 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials c
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | N08801 |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 5552G |
| Place of Origin: | USA |
Description
MATERIAL TECHNICAL STANDARD - UNS N08801
MATERIAL CATEGORY - High Alloy Aerospace Material Steel Series
TECHNICAL SPECIFICATION - AMS 5552G
HS CODE - 72221100 / 72221900 / 72223000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): ≤ 0.10
Mn (％): ≤ 1.50
Si (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 19.0 ~ 22.0
Ni (%): 30.0 ~ 34.0
Mo (％): -
Co (%): ≤ 1.00
Ti (％): 0.75 ~ 1.50
Al (％): -
Cu (%): ≤ 0.50
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: bars and forgings
Tensile strength, σb/MPa: 550 ~ 725
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness + solution annealed (HB): -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
MATERIAL CATEGORY - High Alloy Aerospace Material Steel Series
TECHNICAL SPECIFICATION - AMS 5552G
HS CODE - 72221100 / 72221900 / 72223000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): ≤ 0.10
Mn (％): ≤ 1.50
Si (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 19.0 ~ 22.0
Ni (%): 30.0 ~ 34.0
Mo (％): -
Co (%): ≤ 1.00
Ti (％): 0.75 ~ 1.50
Al (％): -
Cu (%): ≤ 0.50
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: bars and forgings
Tensile strength, σb/MPa: 550 ~ 725
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness + solution annealed (HB): -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.