AMS 6498
Description AMS 6498 datasheet, AMS 6498 Chemical, AMS 6498 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Mi
| Product parameters | |
| Material Category:: | Structure Steel |
| Steel Grade: | AMS 6498 |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 9498A |
| Place of Origin: | USA |
Description
MATERIAL TECHNICAL DATASHEET - AMS 6498
MATERIAL TYPE: 1.4Cr-1.2Mo-0.3V Low alloy steel
MATERIAL STANDARDS - AMS 9498A
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.29 ~ 0.36
Si (％): ≤ 0.30
Mn (％): 0.70 ~ 1.20
P (％)≤: 0.015
S (％)≤: 0.005
Cr (%): 1.10 ~ 1.60
Mo (%): 0.90 ~ 1.40
Ni (%): 0.50 ~ 1.00
V (%): 0.20 ~ 0.40
Al (%): 0.10 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 1250
Yield strength, σ0.2/MPa: 1070
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 375 ~ 450
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR / VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL TYPE: 1.4Cr-1.2Mo-0.3V Low alloy steel
MATERIAL STANDARDS - AMS 9498A
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.29 ~ 0.36
Si (％): ≤ 0.30
Mn (％): 0.70 ~ 1.20
P (％)≤: 0.015
S (％)≤: 0.005
Cr (%): 1.10 ~ 1.60
Mo (%): 0.90 ~ 1.40
Ni (%): 0.50 ~ 1.00
V (%): 0.20 ~ 0.40
Al (%): 0.10 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 1250
Yield strength, σ0.2/MPa: 1070
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 375 ~ 450
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR / VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.