Inventory AMS 5589E Specifications, AMS 5589EV Datasheet, Chemical AMS 5589E Stocklist from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of th
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | AMS 5589E |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 5589D |
| Place of Origin: | USA |
Description
TECHNICAL SPECIFICATIONS - AMS 5589E
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5589D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
Chemical Compositions (Mass weight %)
C (％): ≤ 0.08
Si (％): ≤ 0.35
Mn (％): ≤ 0.35
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 17.0 ~ 21.0
Co (%): ≤ 1.00
Mo (％): 2.80 ~ 3.30
Nb/Ta (％): 4.75 ~ 5.50
Ti (%): 0.65 ~ 1.15
Al (%): 0.20 ~ 0.80
B (%): ≤ 0.006
Fe (%): Remainder
Cu (%): ≤ 0.30
Ni (%): 50.0 ~ 55.0
Ta (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bars, plate, and forgings
Heat treatment condition: solution annealing treated
Tensile strength, σb/MPa: 1069
Yield strength, σ0.2/MPa: 655
Elongation, δ(％): 30.0
Reduction of area, ф (％): -
Hardness | HRW: 363 Max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD, VOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5589D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
Chemical Compositions (Mass weight %)
C (％): ≤ 0.08
Si (％): ≤ 0.35
Mn (％): ≤ 0.35
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 17.0 ~ 21.0
Co (%): ≤ 1.00
Mo (％): 2.80 ~ 3.30
Nb/Ta (％): 4.75 ~ 5.50
Ti (%): 0.65 ~ 1.15
Al (%): 0.20 ~ 0.80
B (%): ≤ 0.006
Fe (%): Remainder
Cu (%): ≤ 0.30
Ni (%): 50.0 ~ 55.0
Ta (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bars, plate, and forgings
Heat treatment condition: solution annealing treated
Tensile strength, σb/MPa: 1069
Yield strength, σ0.2/MPa: 655
Elongation, δ(％): 30.0
Reduction of area, ф (％): -
Hardness | HRW: 363 Max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD, VOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.