Specifications A514 GRADE A datasheet, A514 GRADE A Chemical, A514 GRADE A Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of the
| Product parameters | |
| Material Category:: | Structure Steel |
| Steel Grade: | A514 GRADE A |
| Material Technical Standards:: | ASTM |
| Specification Code:: | ASTM A514 |
| Place of Origin: | USA |
Description
TECHNICAL DATA SHEET - ASTM A514 GRADE A
MATERIAL CATEGORY: Low alloy Series steel
MATERIAL SPECIFICATIONS - ASTM A514
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.15 ~ 0.21
Si (％): 0.40 ~ 0.80
Mn (％): 0.80 ~ 1.10
P (％)≤: 0.030
S (％)≤: 0.025
Cr (%): 0.50 ~ 0.80
Mo (%): 0.18 ~ 0.28
Zr (%): 0.05 ~ 0.15
B (%): 0.0025 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/MPa: 765
Yield strength, σ0.2/MPa: 690
Elongation, δ(％): 18.0
Reduction of area, ф(％): -
Hardness (HBW): 289 max.
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5 to 450mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL(sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL CATEGORY: Low alloy Series steel
MATERIAL SPECIFICATIONS - ASTM A514
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.15 ~ 0.21
Si (％): 0.40 ~ 0.80
Mn (％): 0.80 ~ 1.10
P (％)≤: 0.030
S (％)≤: 0.025
Cr (%): 0.50 ~ 0.80
Mo (%): 0.18 ~ 0.28
Zr (%): 0.05 ~ 0.15
B (%): 0.0025 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/MPa: 765
Yield strength, σ0.2/MPa: 690
Elongation, δ(％): 18.0
Reduction of area, ф(％): -
Hardness (HBW): 289 max.
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5 to 450mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.