1.3815 Round bar ISO9001 approval
| Product parameters | |
| Material Category:: | Austenitic Non-magnetic Stainless Steel |
| Stocklist & Inventory Available:: | Diameter 60 ~ 200mm |
| Melting Process Route:: | BEF + AOD / +ESR |
| Min. order quantity Per Batch:: | 200 kgs |
| Production Lead Time:: | Within 15 days after 30% deposit prepayable |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
Material Catetory - Non-magnetic stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Stock Available - Round bar Diameter 60 ~ 210mm
Chemical Elements (mass weight - %)
Carbon, C (％): ≤ 0.12, Silicon, Si (％): ≤ 1.00, Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.050, Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.5 ~ 20.0, Nickel, Ni (％): ≤ 0.30, Vanadium, V (％): ≤ 0.20
Aluminum, Al (％): ≤ 0.10, Niobium, Nb (％): ≤ 0.25, Nitrogen, N (％): ≥ 0.55
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Solution treatment temperature: 1050 ℃
Tensile strength, σb≥ /MPa: 500 ~ 750
Yield strength, σ0.2 ≥/MPa: 285
Elongation, δ≥(％): 15.0
Impact strength, Akv ≥/J: -
Material Specifications - DIN SEW 390 (1991)
Stock Available - Round bar Diameter 60 ~ 210mm
Chemical Elements (mass weight - %)
Carbon, C (％): ≤ 0.12, Silicon, Si (％): ≤ 1.00, Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.050, Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.5 ~ 20.0, Nickel, Ni (％): ≤ 0.30, Vanadium, V (％): ≤ 0.20
Aluminum, Al (％): ≤ 0.10, Niobium, Nb (％): ≤ 0.25, Nitrogen, N (％): ≥ 0.55
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Solution treatment temperature: 1050 ℃
Tensile strength, σb≥ /MPa: 500 ~ 750
Yield strength, σ0.2 ≥/MPa: 285
Elongation, δ≥(％): 15.0
Impact strength, Akv ≥/J: -