Z12CNDV12-03 Round bar Stock Available
| Product parameters | |
| Material Category:: | Martensitic Hardening Stainless Steel |
| Specification Code:: | NF A35-578 - 1991 |
| Terms of Price:: | Ex works, CIF, and CFR |
| Min. order quantity Per Batch:: | 200 KG |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
Description
TECHNICAL DATA SHEET - NF Z12CNDV12-02
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant Steel
TECHNICAL SPECIFICATIONS - NF A35-578 - 1991
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.08 ~ 0.15
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Ni (％): 2.00 ~ 3.00
Mo (%): 1.50 ~ 2.00
V (%): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, TS σb/≥ MPa: 950 ~ 1150
Yield strength, YS σ0.2/≥ MPa: 800
Elongation, EL δ ≥(％): 13.0
Hardness via heat treatment / HBW: 269 ~ 340
INVENTORY STOCKLIST - Diam.80mm / 90mm
DESCRIPTION
The alloy is usually produced by EAF + VD + LF or VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - Q + T + SRA.
If you meet further on any technical enquiry or help, you can E-MAIL (sales@cnlhss.com) our qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant Steel
TECHNICAL SPECIFICATIONS - NF A35-578 - 1991
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.08 ~ 0.15
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Ni (％): 2.00 ~ 3.00
Mo (%): 1.50 ~ 2.00
V (%): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, TS σb/≥ MPa: 950 ~ 1150
Yield strength, YS σ0.2/≥ MPa: 800
Elongation, EL δ ≥(％): 13.0
Hardness via heat treatment / HBW: 269 ~ 340
INVENTORY STOCKLIST - Diam.80mm / 90mm
DESCRIPTION
The alloy is usually produced by EAF + VD + LF or VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - Q + T + SRA.
If you meet further on any technical enquiry or help, you can E-MAIL (sales@cnlhss.com) our qualified production engineers.