X11CrNiMoN12 Flat bar Available Stock
| Product parameters | |
| Material Category:: | Martensitic Stainless Steel Series |
| Material Technical Standards:: | DIN EN 10302 / 10269 / 10095 |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Diameter 55 ~ 320mm |
| Min. order quantity Per Batch:: | 500 KG |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308. |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
Introduction:
X11CrNiMoN12 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
X11CrNiMoN12 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X11CrNiMoN12 used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X11CrNiMoN12 used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
| DIN | W-Nr | Other |
|---|---|---|
| X11CrNiMoN12 | W-Nr 1.4938 | 1.4939 |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| 0.08 ～ 0.15 | ≤ 0.50 | 0.40 ～ 0.90 | ≤ 0.025 | ≤ 0.015 | 11.0 ～ 12.5 | 2.00 ～ 3.00 | 1.50 ～ 2.00 | V 0.25 ～ 0.40 V 0.010 ～ 0.040 |
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | - | - | - | - | - | - |
| Q/T | 950 ～ 1150 | ≥ 800 | ≥ 13.0 | - | ≥ 55 | - |