Contact Us
East district of New high-tech industrial park, Jiangyou City, Sichuan Province, China
86 - 15386611557
www.cnlhss.com

AE961W Round bar Available Stock

Description AE961W Stock list Round bars AE961W, Suppliers  Inventory Sheet & plate from Steel melting (ESR refined), Blooming, Hot  forging, Hot rolling, Heat treatment,
Product parameters
Material Category:: Martensitic Stainless Steel Series
Stocklist & Inventory Available:: Diameter 10 ~ 220mm
Melting Process Route:: EAF + VD + LF / BEF + ESR
Min. order quantity Per Batch:: 500 kg
Certification:: Commercial Invoice, Packing list, CO, Bill of lading, Origin of Certificate, Form E
Ultrasonic Test Standard:: ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308
Production Lead Time:: Within 15 days after 30% downpayment.
Unified Social Credit Code:: 91510871777942750J
Company ISO Register No:: UQ211218R0
INQUIRY
Description

Martensitic stainless steel AE961W / GB 1Cr11Ni2W2MoV is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc.

The
alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment.

With 20 years of accumulated know-how, we have confidence in Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special 
material is welcome.

We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.

Material Technical Specification - Grade AE961W
Material Category - Heat resisting 
steel for Turbine blade processing 
Inventory & Stocklist - Round bar diameter 15 ~ 200mm

Chemical Composition (Mass weight %) - AE961W
C (%): 0.10 ~ 0.16, Si (%): ≤ 0.60, Mn (%):≤ 0.60, P (%)≤: 0.035, S (%)≤: 0.010
Cr (%): 10.5 ~ 12.0, Mo (%): 0.35 ~ 0.50, Ni (%): 1.40 ~ 1.80
V (%): 0.18 ~ 0.30, W (%): 1.50 ~ 2.00
Fe (%): balance

Typical Mechanical Properties AT RM
Contion: QT1 (Tempering 660 ~ 710 Deg. C)
Tensile strength,σb/≥ MPa: 885
Yield strength, σ0.2/≥ MPa: 738
Elongation, δ ≥(%): 15.0
Reduction of area, (%): 55.0
Impact, AKu/J ≥: 71
QT hardness, HB ≤: 269 ~ 311

Contion: QT2 (Tempering 540 ~ 590 Deg.C)
Tensile strength,σb/≥ MPa: 1080
Yield strength, σ0.2/≥ MPa: 885
Elongation, δ ≥(%): 12.0
Reduction of area, (%): 50.0
Impact, AKv/J ≥: 55
QT hardness, HB ≤: 311 ~ 388

Submit an enquiry for the displaying steel materials you are interested in TODAY!