Martensitic Steels Z12CNDV12-03 Forged Parts Machining
Z12CNDV12-03 is Martensitic Stainless steel that should be hardened to achieve excellent mechanical properties by different tempering temperatures. The steel achieved high strength and hardness after final treatment.
| Product parameters | |
| Specification Code:: | NF A35-578 - 1991 |
| Stocklist & Inventory Available:: | Diameter 55 ~ 220mm |
| Melting Process Route:: | BEF + AOD /+ ESR |
| Min. order quantity Per Batch:: | 1300 KG |
| Heat Treatment Practice:: | Hardened 1050 ℃, water or air cooled, tempered 640 ~ 690 ℃, double tempered |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Standard Export Packing Way:: | Wooden box / tray / pallet free from fumigation |
| Production Lead Time:: | Within 45 days after payment |
Description
Z12CNDV12-03 is Martensitic Stainless steel that should be hardened to achieve excellent mechanical properties by different tempering temperatures. The steel achieved high strength and hardness after final treatment.
Chemical Composition (Mass weight - %) - Z12CNDV12-03
C (％): 0.08 ~ 0.15, Si (％): ≤ 0.35, Mn (％): 0.50 ~ 0.90, P (％)≤: 0.030, S (％)≤: 0.010
Cr (％): 11.0 ~ 12.5, Ni (％): 2.00 ~ 3.00, Mo (%): 1.50 ~ 2.00, V (%): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05, Fe (%): balance
Mechnical Properties under room temperature
Hardened: 1040 Deg. C, 3h, termpered 650 Deg. C, air cooled
Tensile strength, TS σb/≥ MPa: 930 ~ 1150
Yield strength, YS σ0.2/≥ MPa: 780
Elongation, EL δ ≥(％): 13.0
hardness / HBW: 340 Max.
Product Description
The alloy is usually produced by AOD / EAF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - Q + T + STR
Typical Applications
Chemical equipment & pats.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade.
Bolt and nut, Valve, Pressure vessel.